enameled aluminum wire – xinyu-enameledwire.com
- Street: No. 88, Chuangju Road, Qidu Town, Wujiang, Suzhou Jiangsu Province, China
- City: suzhou
- State: jiangsu
- Zip/Postal Code: 215000
- Listed: January 12, 2018 2:37 am
Description
Characteristic: The Enameled Aluminum Wire has excellent properties of mechanical strength .film adhesion and solvent resistance,light weight and flexibility.lt is widely used in transformers,inductors,ballasts.electrial appliances, deflection coils in display,antimagnetized coils,induction cooker,microwave oven,reactor,etc.
Standard in accordance with : IEC 60317-0-3:2008
Type: QZL-2/130
XINYU ELECTRICAL 130 Enameled Aluminum Wire : http://www.xinyu-enameledwire.com/product/enameled-aluminum-wire/
PRODUCT: Enameled Wire
STANDARD:IEC 60317-0-3:2008
DATE:10th,Jul.,2017
TYPE:QZL-2/130
SIZE:1.800mm
TESTING ITEMS Refer to REQUIREMENT TESTING DATA RESULTS
1 Appearance IEC 60317-0-3:2008 3.3 Smooth Surface Qualified Qualified
2 Conductor Dimension IEC 60317-0-3:2008 4.1 1.800±0.018mm 1.799 Qualified
3 Over-all Diameter IEC 60317-0-3:2008 4.4.1 ≤1.909mm 1.885 Qualified
4 Minimum Film Thickness IEC 60317-0-3:2008 4.3.1 ≥0.073mm 0.086 Qualified
5 Elongation IEC 60317-0-3:2008.6 ≥15﹪ 27 Qualified
6 Electrical Resistance (20℃) IEC 60317-0-3:2008.5 0.0106-0.0113 Ω/m 0.0108 Qualified
7 Breakdown Voltage (Room Temperature) IEC 60317-0-3:2008.13 ≥ 5.0KV 7.2, 8.0, 7.8, 7.4, 8.5 Qualified
8 Tensile Strength IEC 60317-0-3:2008.6 ≥ 80 N/mm2 97 Qualified
9 Tension Test IEC 60317-0-3:2008 8.2 Stretch 15%,
Coating No Crack No Crack Qualified
10 Heat Shock IEC 60317-0-3:2008.9 155℃*30min, Coating No Crack (Stretch 15%) No Crack Qualified
11 Solvent Test IEC 60317-0-3:2008 12 “H” No Crack Qualified
12 RoHS Confirmation RoHS Requirement Qualified Qualified
Here are a number of route introductions for xinyu-enameledwire.com.
Shanghai Hongqiao Airport ……………………… 1.0h Drive
Shanghai Pudong International Airport ………… 1.5h Drive
Hangzhou Xiaoshan Airport ……………………… 2.0h Drive
SuNan ShuoFang International Airport ………… 2.0h Drive
Huzhou High-speed Railway Station …………… 45min Drive
Suzhou High-speed Railway Station …………… 1.5h Drive
Hangzhou High-speed Railway Station ………… 2.0h Drive
China Enameled Aluminum Wire: http://www.xinyu-enameledwire.com/
600 total views, 2 today